Longitudinal Test (Before Gray Tracking Test ):
It appears that the absorption of GTR-KTP at 1064nm is only 1/10 of conventional KTP.
Gray Tracking Test:
When a green laser beam(400mW, beam diameter 0.07mm, power density 10KW/cm2) goes through the crystal, it causes an increase in the IR absorption of the crystal. This phenomenon is correlated with “gray tracking effect”. The following graphs show the different absorption levels at 1064nm between CASTECH’s GTR KTP and the conventional KTP.
Transverse scan after gray tracking test (at 1064 nm):
Transverse scan after gray tracking test (at 532 nm) :
Damage threshold testing：
After testing a group of GTR-KTP and the conventional KTP crystals (polished only) with laser condition of 10ns, 1 HZ, we found that CASTECH's GTR-KTP has laser damage threshold around 1.8GW/cm2 at 1064nm, which is much higher than the conventional KTP (450MW/cm2 in the same condition).
Transmission curve in the visible and UV region:
Apparently CASTECH's GTR-KTP has lower absorption than the conventional KTP in the range of 350-550nm. We can conclude that CASTECH's GTR-KTP is expected to have a higher gray track resistance than the regular flux grown KTP crystals.
CASTECH provides the following AR-coatings：
? IBS, IAD or E-beam coating methods are available upon request.
? Dual Band AR-coating (DBAR) of GTR-KTP for SHG of 1064nm.
low reflectance (R<0.2% at 1064nm and R<0.5% at 532nm );
high damage threshold (>1.2GW/cm2 at 1064nm, >300MW/cm2 at 532nm, at 10ns, 2.5Hz); long durability.
? Broad Band AR-coating (BBAR) of GTR-KTP for OPO applications.
? High reflectivity coating: HR1064nm&HT532nm, R>99.8%@1064nm, T>95%@532nm.
? Other coatings are available upon request.
CASTECH offers GTR-KTP with：
? Strict quality control;
? Large crystal size up to 7x7x20mm3 ;
? Quick delivery (2 weeks for polished only, 3 weeks for coated);
? Unbeatable price and quantity discount ;
? Technical support;
? AR, HR-coating, mounting and re-polishing service.
CASTECH's Warranty on GTR-KTP Specifications：
? Dimension tolerance： (W±0.1mm)x(H±0.1mm)x(L+0.5/-0.1mm) (L≥2.5mm)
? Clear aperture: central 90% of the diameter
? No visible scattering paths or centers when inspected by a 50mW green laser
? Flatness: less than λ/8 @ 633nm
? Transmitting wavefront distortion: less than λ/8 @ 633nm
? Chamfer： ≤0.2mmx45°
? Scratch/Dig code: better than 10/5(polished only) to MIL-PRF-13830B
better than 20/10(AR-coated) to MIL-PRF-13830B
better than 40/20(HR-coated) to MIL-PRF-13830B
? Parallelism: better than 20 arc seconds
? Perpendicularity: ≤5 arc minutes
? Angle tolerance: ≤0.25°